高铬铸铁标准规范 Standard Specification for high chromium cast iron
参考标准 Reference Standard （ISO 21988-2005）	化学成分 Nominal Chemical Composition (W%)									对应国际标准 Eqv. Standards
参考标准 Reference Standard （ISO 21988-2005）	C	Si	Mn	Ni	Cr	Mo	Cu	P	S	对应国际标准 Eqv. Standards
ISO 21988/JN/ HBW555XCr13	1.8-3.6	≤1.0	0.5-1.5	≤2.0	11.0-14.0	≤3.0	≤1.2	≤0.08	≤0.08	EN-GJN-HV600(XCr11) ASTM A532 12% Cr
ISO 21988/JN/ HBW555XCr16	1.8-3.6	≤1.0	0.5-1.5	≤2.0	14.0-18.0	≤3.0	≤1.2	≤0.08	≤0.08	EN-GJN-HV600(XCr14) ASTM A532 15% Cr-Mo AS 2027 CrMo 15 3 G-X 300 CrMoNi 15 2 1
ISO 21988/JN/ HBW555XCr21	1.8-3.6	≤1.0	0.5-1.5	≤2.0	18.0-23.00	≤3.0	≤1.2	≤0.08	≤0.08	EN-GJN-HV600(XCr18) ASTM A532 20% Cr-Mo AS 2027 CrMo 20 1 G-X 260 CrMoNi 20 2 1
ISO 21988/JN/ HBW555XCr27	1.8-3.6	≤1.0	0.5-2.0	≤2.0	23.0-30.0	≤3.0	≤1.2	≤0.08	≤0.08	EN-GJN-HV600(XCr23) ASTM A532 25% Cr-Mo AS 2027 Cr27 LC & Cr27 HC G-X 260 Cr27
ISO 21988/JN/ HBW600XCr35	3.0-5.5	≤1.0	1.0-3.0	≤1.0	30.0-40.0	≤1.5	≤1.2	≤0.06	≤0.06	AS 2027 Cr35
ISO 21988/JN/ HBW600XCr20Mo2Cu	2.6-2.9	≤1.0	≤1.0	≤1.0	18.0-21.0	1.4-2.0	0.8-1.2	≤0.06	≤0.06	AS 2027 CrMoCu 20 2 1

镍硬铸铁标准规范 Standard Specification for Ni-Hard Cast Iron
参考标准 Reference Standard （ISO 21988-2005）	化学成分Nominal Chemical Composition (W%)							对应国际标准 Eqv. Standards
参考标准 Reference Standard （ISO 21988-2005）	C	Si	Mn	P	S	Ni	Cr	对应国际标准 Eqv. Standards
HBW480Cr2	2.5-3.0	≤0.8	≤0.8	≤0.10	≤0.10	3.0-5.5	1.5-3.0	BTM Ni4Cr2-DT EN-GJN-HV520 AS2027 NiCr2-500 ASTM A 532 Ni-Cr-Lc G-X 260 NiCr 4 2
HBW500Cr9	2.4-2.8	1.5-2.2	0.2-0.8	≤0.06	≤0.06	4.0-5.5	8.0-10.0	EN-GJN-HV550 Ni-Cr-Hc AS2027 NiCr1-550 G-X 330 NiCr 4 2
HBW510Cr2	3.0-3.6	≤0.8	≤0.8	≤0.10	≤0.10	3.0-5.5	1.5-3.0	BTM Ni4Cr2-GT AS2027 NiCr4-500 ASTM A532 C1-B Ni-Cr-Hc ASTM A532 C1-C Ni-Cr-GB
HBW555Cr9	2.5-3.5	1.5-2.5	0.3-0.8	≤0.08	≤0.08	4.5-6.5	8.0-10.0	BTM Cr9Ni5 EN-GJN-HV600 AS2027 NiCr4-600 G-X 300 CrNiSi9 5 2
HBW630Cr9	3.2-3.6	1.5-2.2	0.2-0.8	≤0.06	≤0.06	4.0-5.5	8.0-10.0	BTM Cr9Ni5 AS2027 NiCr4-630 ASTM A532 C1-D Ni-HiCr

铬钼合金钢标准规范 Standard Specification for Cr-Mo Alloy Steel
参考标准 Reference Standard	化学成分 Nominal Chemical Composition (W%)
参考标准 Reference Standard	C	Si	Mn	P	S	Ni	Cr	Mo
AS 2074/L2A	0.45-0.55	≤0.75	0.50-1.00	≤0.04	≤0.04	-	0.80-1.20	-
AS 2074/L2B	0.55-0.65	≤0.75	0.50-1.00	≤0.04	≤0.04	-	0.80-1.50	0.2-0.4
AS 2074/L2C	0.70-0.90	≤0.75	0.50-1.20	≤0.04	≤0.04	-	1.30-2.40	0.2-0.4
ZG42Cr2Si2MnMo	0.38-0.48	1.5-1.8	0.8-1.2	≤0.04	≤0.04	-	1.8-2.2	0.2-0.6
ZG45Cr2Mo	0.40-0.48	0.8-1.2	0.4-1.0	≤0.04	≤0.04	≤0.5	1.7-2.0	0.8-1.2
ZG30Cr5Mo	0.25-0.35	0.4-1.0	0.5-1.2	≤0.04	≤0.04	≤0.5	4.0-6.0	0.2-0.8
ZG40Cr5Mo(FED4A)	0.35-0.45	0.4-1.0	0.5-1.2	≤0.04	≤0.04	≤0.5	4.0-6.0	0.2-0.8
ZG50Cr5Mo	0.45-0.55	0.4-1.0	0.5-1.2	≤0.04	≤0.04	≤0.5	4.0-6.0	0.2-0.8
ZG60Cr5Mo	0.55-0.65	0.4-1.0	0.5-1.2	≤0.04	≤0.04	≤0.5	4.0-6.0	0.2-0.8
FMU-29	0.25-0.45	0.3-1.0	0.6-1.5	≤0.04	≤0.04	-	6.0-8.0	0.2-0.4
FMU-11	0.90-1.30	0.3-1.0	0.6-1.5	≤0.04	≤0.04	-	11.0-13.0	0.3-0.5
FED-13	0.80-1.30	0.4-1.2	0.8-1.5	≤0.04	≤0.04	-	11.0-13.0	0.4-0.8
FED-14	1.60-2.00	0.4-1.2	0.8-1.5	≤0.04	≤0.04	-	11.0-13.0	0.6-1.0

性能 · 特点

硬度：高铬铸铁、镍硬铸铁：≥HRC56；珠光体铬钼合金钢：≥HB310;

冲击韧性值：白口铸铁：AK≥5J；珠光体铬钼合金钢：AK≥60J(常温，无缺口)

球磨机衬板用于保护磨机筒体免受研磨体和矿石的直接冲击和摩擦。同时，可以使用不同的衬板来调节研磨体的运动状态，从而增强研磨体对物料的研磨效果，提高磨机的研磨效率，增加产量，减少研磨量和金属消耗。

按国际标准生产高品质的水泥磨衬板：GB/T26651,GB/T8263-1999,AS2074, AS2027, DIN 1695, AISI,ASTM,JIS G 5153,NF A32401,BS4844。

根据具体工况为您选择合适的矿山磨材质，提高磨机的生产效率，减少衬板和磨球的磨耗。